LINCOLN® ER410 provides air-hardening weld deposits to impart corrosion, erosion, abrasion resistance. Features Designed to weld stainless steels of similar chemical composition as well …

Alloy ER 410 is used to weld Types 403, 405, 410, 416. It is also used for welding overlay on carbon steels to resist corrosion, erosion, or abrasion. ER 410 is an air hardening type filler metal that calls for preheating of the joint to 350ºF before welding. Alloy ER 410 is a Stainless Steel TIG, MIG and SUB-ARC wire used for welding.

Pinnacle Alloys ER410 typical applications include welding and repairing 12% Cr air- hardenable stainless steel like 410, 416, 420, 431, and cast C-15. It is also used for deposition of overlays on carbon steels to resist corrosion, erosion, or abrasion.

ER410 is used for welding types 403, 405, 410, 414, and 416. Also an overlay on carbon steels for corrosion, erosion and abrasion resistance. It is recommended using 350ºF preheat before welding. Data is typical for ER410 weld metal deposited by Mig using Argon + …

AT-ER410不锈钢焊丝 主要成分是13Cr，为马氏体不锈钢TIG焊丝。 焊接顺畅、成形美观，熔敷金属耐腐蚀性良好。 AT-ER410不锈钢焊丝 常应用于耐磨耐蚀的马氏体不锈钢焊接，如12Cr13 (SUS 410)。 1.保护气体：采用纯Ar；流量：电流在100~200A时9~14L/min，电流在200~300A时14~18L/min。 2.钨极伸出长度：3~5mm；电弧长度：1~3mm。 3.风速限制在≤1.0m/s；建议在焊接区背面通氩气保护。 4.在焊接中，焊接线能量的大小直接影响焊缝金属的力学性能及抗裂性 …

TEST RESULTS Test results for mechanical properties, deposit or electrode composition and diffusible hydrogen levels were obtained from a weld produced and tested according to …

ER410 用途:用于水电站以及阀门等耐磨耐蚀场合，如：1Cr13（SUS410）。

ER410，及该型号钢材的基本信息、化学元素成分、机械性能、力学性能、热处理温度、同等型号参照表等

ER410 is a filler wire is used to join similar base metals and for welding overlay on carbon steels. This alloy contains higher amount of carbon that enables air-hardening, producing a …

焊丝主要成分是13Cr，为马氏体不锈钢MIG焊丝，可全位置焊接。 焊接作业性极佳——送丝顺畅、电弧稳定、成形美观、飞溅极少。 常应用于水电站以及阀门等耐磨耐蚀场合，如12Cr13 (SUS 410)。 1.保护气体：注意保护气体的纯度，混合气配比推荐Ar+1~3%O2。 2.气体流量：20~25L/min。 3.干伸长度：15~25mm。 4.将焊接部位的锈层、湿气、油污、灰尘等确实除净。 5.室外施焊时，当风速大于1.5m/s应采取防风措施，须有适当的防风措施，以防发生气孔。 以 …